Reversol P-9770P is a pre-promoted, thixotropic isophthalic unsaturated polyester resin developed for the manufacture of laminates for use in a wide range of critical applications where a tough, high performance water and chemical resistant resin is required. This resin can be applied by brush or spray equipment and may also be used for non-digging sewage pipe system. When fully cured and post cured, Reversol P-9770P is resistant to fuel oils and other similar chemicals.

Available Documents

TDS Download

Technical Informations

Application Advice/Typical Applications

( *Test methods as in BS 2782 : The curing schedule was 12 hrs at 30°C followed by 12hrs at 50°C + 3 hrs at 80°C) (** Test methods as in BS-2782 : The curing schedule was 12 hrs at 30°C followed by 2 hrs at 80°C + 2 hrs at 120°C)

High performance FRP tanks and containers FRP Boat construction Cure in-place pipe (CIPP)

Shipping and Storage

To ensure maximum stability and maintain optimum resin properties, Reversol P-9770P should be stored in closed containers below 32°C and away from heat sources and sunlight. All storage should conform to local fire and building codes. Drums should be stored away from all sources of flame or combustion. Inventory should be maintained at minimum reasonable stock and used on a first-in-first-out basis. When properly stored, Reversol P-9770P will remain stable for 3 months from date of delivery.

Product Security/Health and Safety

Before handling, please read the Safety Data Sheet of this product for advice on safety, use and disposal.

Effluents and Pollution Control

Before handling, please read the Safety Data Sheet of this product for advice on safety, use and disposal.

For further information regarding this product please refer to:

Synthomer Limited Head Office
Phone: +44 (0)1279 436 211
FAX: +44 (0)1279 444 025
eMail: info@synthomer.com


Properties

Character Value Unit
Appearance Pinkish orange  
Non-Volatile 59 ± 2
Viscosity@ 25 °C - Brookfield #3/6 1200-1600 cps 
Viscosity@ 25 °C - Brookfield #3/60 400-700 cps 
Thixotropic Index 1.2 – 2.0  
Geltime @ 25 °C - 100g esin + 1ml MEKP 30 – 40 minute 
Acid Value 30 mg KOH/g 
Specific Gravity 1.1  
Volumetric Shrinkage 7.5
Tensile Strength *79.8 MPa 
Tensile Strength **80 MPa 
Tensile Modulus *4018 MPa 
Tensile Modulus **--- MPa 
Elongation at Break *3.5
Elongation at Break **2.3
Flexural strength *129 MPa 
Flexural strength **151 MPa 
Flexural Modulus *3682 MPa 
Flexural Modulus **4700 MPa 
Compression Strength *129 MPa 
Compression Strength **--- MPa 
Compression Modulus *2600 MPa 
Compression Modulus **--- MPa 
Water Absorption 24 hr at 25°C *9.5 mg 
Water Absorption 24 hr at 25°C **--- mg 
Deflection Temperature (under load 1.80 MPa) *71 °C 
Deflection Temperature (under load 1.80 MPa) **77 °C 
Barcol Hardness (Model GYZJ 934-1) *46  
Barcol Hardness (Model GYZJ 934-1) **47  


© 2014 Synthomer plc

Home » Markets & Products » Productfinder » Products A-Z » Technical datasheet

  • Paper & Board
  • Construction & Coatings
  • Health & Protection
  • Carpet, Compounds & Foam
  • Functional Polymers
  • Performance Polymers
  • Productfinder
  •     Products A-Z
  •     Products by Specifications